SKYPRENE TSR-41

Chloroprene Rubber (CR, commonly referred to as Neoprene) is widely specified across demanding industrial rubber applications due to its balanced combination of tensile strength, oil resistance, thermal stability, and weatherability. However, selecting the optimal CR grade requires aligning chemical modification types and raw polymer viscosity with processing methods and cold-weather endurance requirements.     1. General-Purpose Grades Skyprene general-purpose grades are mercaptan-modified polymers offering excellent mechanical strength, oil and weather resistance, and dynamic resilience. SKYPRENE B-30 (Standard Baseline): Featuring a medium Mooney viscosity (ML1+4 100℃ = 49), B-30 offers balanced physical properties (Tensile Strength Ta = 23.1 MPa, Elongation Ea = 390%) and good storage stability. Ideal for molded parts, belts, and industrial hoses. SKYPRENE B-31 (Low Viscosity, High Flowability): A low-viscosity variant (ML1+4 = 42) of B-30. Lower Mooney viscosity reduces frictional heat generation during mill mixing, improving dimensional stability and processing speed in extrusion, injection, and high-speed calendering. SKYPRENE Y-30S & Y-31 (High Viscosity & Ultra-High Filler Loadings): Y-30S possesses an exceptionally high Mooney viscosity (ML1+4 = 127). It permits compounding with high volume fractions of carbon black/fillers and process oils without compromising tensile strength (23.8 MPa), drastically reducing formulation costs. Y-31 (ML1+4 = 100) provides improved processability and fluidity over Y-30S, making both grades premier choices for high-strength solvent-based industrial adhesives. SKYPRENE P-90 (Xanthogen-Modified): Xanthogen-modified grade providing elevated mechanical modulus and higher tensile strength (26.0 MPa). Its crystallization rate is slightly faster than B-30, allowing rapid green strength development for dynamic high-load applications.   2. Crystallization-Resistant Grades Under sub-zero operational temperatures, standard CR polymers tend to undergo molecular alignment (crystallization), resulting in physical hardening and elasticity loss. Crystallization-resistant grades introduce structural irregularity into the polymer chain to suppress crystal growth. SKYPRENE B-5 & B-5A (Extreme Cold Endurance): B-5 and B-5A offer superior resistance to crystallization. B-5A exhibits the lowest permanent set at -10℃ (7%, compared to 36% for B-30), ensuring zero hardening and optimal sealing pressure in sub-zero operational environments. SKYPRENE B-10, B-10H, B-11, B-12 (Graded Resistance) : Positioned between B-30 and B-5 in crystallization rate. Compounders can select specific Mooney viscosities ranging from B-12 (ML = 39) for easy molding, B-10/B-11 (ML = 46-52) for standard processing, up to B-10H (ML = 70) for high structural green strength. SKYPRENE B-25 (High Elongation): Balances medium crystallization resistance with superior tensile elongation (410%), ideal for flexible boots, bellows, and seals operating in cold climates.   3. Injection Molding Grades Automated rubber injection molding demands low mold fouling, zero premature scorch in hot runners, fast mold filling, and smooth part demolding. Low Mold Staining & High Flowability: SKYPRENE TSR-41, TSR-42, TSR-44: Low Mooney viscosity variants (ML1+4 = 44-48) engineered for thin-walled or multi-cavity injection molds. They prevent premature vulcanization while offering maximum cavity fill speed and drastically reducing mold cleaning downtime. Enhanced Scorch Safety & Dynamic Resilience: SKYPRENE TSR-44: Delivers an extended Mooney scorch time (t5 = 10.6 min), allowing long residence times in injection barrels without thermal degradation or pre-curing.   4. Extrusion Grades Extruded profile seals, continuous rubber hoses, cable jacketing, and sponge profiles require high green strength to prevent cross-sectional deformation before vulcanization. SKYPRENE Y-20E & E-33 (High Flowability & Surface Finish): Y-20E offers the ultimate extrusion flow performance and is frequently blended with B-10 or B-30 to fine-tune extrusion speeds. E-33 is a xanthogen-modified extrusion grade providing excellent calendering and extrudability combined with high tensile strength (22.6 MPa). SKYPRENE E-20, E-20H, 630, 640 (Collapse Resistance & Viscosity Control): E-20 (ML = 47) and E-20H (ML = 62) feature improved cold crystallization resistance. Grade 630 utilizes an ultra-high Mooney viscosity (ML = 110) to provide maximum resistance to dimensional deformation under continuous steam/hot-air vulcanization. Grade 640 (ML = 81) is a mercaptan-modified variant providing intermediate Mooney viscosity balance.   5. Sulfur-Modified Grades Sulfur-modified grades contain reactive polysulfide links (-Sx-) along their polymer backbones. Compounding shear stresses cleave these bonds (peptization), enabling unique chemical properties unachievable with mercaptan grades. Key Technical Advantages: Superior Dynamic Strength & Toughness: R-22 and R-10 exhibit exceptional tear strength and high ultimate elongation (490%), making them suitable for severe dynamic stress applications like drive belts and rubber linings. Exceptional Substrate Adhesion: Dynamic sulfur linkages promote natural tack and interfacial chemical bonding with metals and synthetic fabric reinforcements. Metal Oxide Curing: Can be vulcanized using metallic oxides (ZnO/MgO) without requiring organic accelerators.   Website: www.elephchem.com whatsapp: (+)86 13851435272 E-mail: admin@elephchem.com